Rate-Dependence of Tensile Properties And Stress-Strain Behavior of an Oxide/ Oxide Ceramic Matrix Composite at Elevated, (Paperback)

Advanced aerospace structures and components require materials that exhibit high strength at high operating temperatures. Nextel " 720/Alumina (N720/A) is an oxide/oxide, porous-matrix ceramic-matrix composite developed for load bearing applications at elevated temperatures. The current research investigates the rate dependence of tensile properties of the N720/A CMC at 1200-C as well as the creep behavior of this composite under applied stresses in the 1-25 MPa range. In addition, influence of prior loading rate on the creep response of N720/A under applied stresses above 50 MPa was evaluated at 1200-C. Tensile tests conducted at loading rate of 0.0025 and 25 MPa/s revealed a strong influence of rate on the ultimate tensile strength, elastic modulus and failure strain. Several samples subjected to additional heat-treatments were tested to ascertain whether the stress-strain behavior observed in the 0-30 MPa stress range in tests conducted at 0.0025 MPa/s was an artifact of incomplete processing of fibers in the as-received material. Additional heat treatment had no effect on stress-strain behavior at 0.0025 MPa/s.

This work has been selected by scholars as being culturally important, and is part of the knowledge base of civilization as we know it. This work was reproduced from the original artifact, and remains as true to the original work as possible. Therefore, you will see the original copyright references, library stamps (as most of these works have been housed in our most important libraries around the world), and other notations in the work.

This work is in the public domain in the United States of America, and possibly other nations. Within the United States, you may freely copy and distribute this work, as no entity (individual or corporate) has a copyright on the body of the work.

As a reproduction of a historical artifact, this work may contain missing or blurred pages, poor pictures, errant marks, etc. Scholars believe, and we concur, that this work is important enough to be preserved, reproduced, and made generally available to the public. We appreciate your support of the preservation process, and thank you for being an important part of keeping this knowledge alive and relevant.